Tooling Block
We provide a comprehensive range of tooling block solutions to match customer requirements.
| TB650 Epoxy syntactic for use as high quality tooling block |
| Property |
Test Method |
Value |
SI Units |
Value |
Imperial Units |
| Color |
|
Green |
|
|
|
| Density |
BS EN ISO 1183-3: 1999 |
680 |
kg/m3 |
43 |
lb/ft3 |
| Shore Hardness |
ISO 868: 1998 |
69 |
°D |
69 |
°D |
| Uniaxial Compressive Strength |
BS EN ISO 604 |
45.5 |
MPa |
6600 |
lbf/in2 |
| Uniaxial Compressive Modulus |
BS EN ISO 604 |
1490 |
MPa |
216100 |
lbf/in2 |
| Heat Distortion Temperature |
BS 2782 |
111 |
°C |
232 |
°F |
| Coefficient of Thermal Expansion |
BS 4618 3.1 |
38.0 |
x10-6/°C |
21.2 |
x 10-6/°F |
| TB620 Epoxy syntactic for use as a cost effective tooling block |
| Property |
Test Method |
Value |
SI Units |
Value |
Imperial Units |
| Color |
|
Blue |
|
|
|
| Density |
BS EN ISO 1183-3: 1999 |
620 |
kg/m3 |
39 |
lb/ft3 |
| Shore Hardness |
ISO 868: 1998 |
69 |
°D |
69 |
°D |
| Uniaxial Compressive Strength |
BS EN ISO 604 |
38.0 |
MPa |
5510 |
lbf/in2 |
| Uniaxial Compressive Modulus |
BS EN ISO 604 |
1200 |
MPa |
174000 |
lbf/in2 |
| Heat Distortion Temperature |
BS 2782 |
110 |
°C |
230 |
°F |
| Coeeficient of Thermal Expansion |
BS 4618 3.1 |
39.0 |
x10-6/°C |
21.7 |
x 10-6/°F |
| TB610 Epoxy Syntactic for high quality tooling block (high Tg) |
| Property |
Test Method |
Value |
SI Units |
Value |
Imperial Units |
| Color |
|
Blue |
|
|
|
| Density |
BS EN ISO 1183-3: 1999 |
623 |
kg/m3 |
39 |
lb/ft3 |
| Shore Hardness |
ISO 868: 1998 |
69 |
°D |
69 |
°D |
| Uniaxial Compressive Strength |
BS EN ISO 604 |
40.0 |
MPa |
5800 |
lbf/in2 |
| Glass Transition Temperature |
BS EN ISO 604 |
158 |
°C |
316 |
°F |
| Coefficient of Thermal Expansion |
BS 4618 3.1 |
28.2 |
x10-6/°C |
15.7 |
x 10-6/°F |
| EP678 Epoxy syntactic for use as high quality tooling block |
| Property |
Test Method |
Value |
SI Units |
Value |
Imperial Units |
| Color |
|
Blue |
|
|
|
| Density |
BS EN ISO 1183-3: 1999 |
708 |
kg/m3 |
44 |
lb/ft3 |
| Uniaxial Compressive Strength |
BS EN ISO 604 |
52.0 |
MPa |
7540 |
lbf/in2 |
| Heat Distortion Temperature |
BS 2782 |
119 |
°C |
246 |
°F |
| Coefficient of Thermal Expansion |
BS 4618 3.1 |
35.7 |
x10-6/°C |
19.9 |
x 10-6/°F |
| EP671 Epoxy syntactic for use as a cost effective tooling block |
| Property |
Test Method |
Value |
SI Units |
Value |
Imperial Units |
| Color |
|
Tan |
|
|
|
| Density |
BS EN ISO 1183-3: 1999 |
609 |
kg/m3 |
38 |
lb/ft3 |
| Shore Hardness |
ISO 868: 1998 |
59 |
°D |
59 |
°D |
| Uniaxial Compressive Strength |
BS EN ISO 604 |
25.8 |
MPa |
3740 |
lbf/in2 |
| Heat Distortion Temperature |
BS 2782 |
63 |
°C |
145 |
°F |
| Coefficient of Thermal Expansion |
BS 4618 3.1 |
60.3 |
x10-6/°C |
33.6 |
x 10-6/°F |
| EP650 Epoxy syntactic for high quality tooling block (high Tg) |
| Property |
Test Method |
Value |
SI Units |
Value |
Imperial Units |
| Colour |
|
Brown |
|
|
|
| Density |
BS EN ISO 1183-3: 1999 |
684 |
kg/m3 |
43 |
lb/ft3 |
| Shore Hardness |
ISO 868: 1998 |
67 |
°D |
67 |
°D |
| Uniaxial Compressive Strength |
BS EN ISO 604 |
40.6 |
MPa |
5890 |
lbf/in2 |
| Heat Distortion Temperature |
BS 2782 |
123 |
°C |
253 |
°F |
| Coefficient of Thermal Expansion |
BS 4618 3.1 |
42.0 |
x10-6/°C |
23.4 |
x 10-6/°F |